Study of Recrystallization Kinetics of 1565ch Aluminum Alloy during hot deformation

The present study addresses recrystallization process in Al-Mg-Mn-Zn-Zr system alloy samples. The samples are collected from cast ingot, produced by casting to industrial DC mold, and homogenized based on standard industrial practice. After that the samples were rolled with different hot rolling sch...

Full description

Saved in:
Bibliographic Details
Published in:MATEC web of conferences 2020, Vol.326, p.5001
Main Authors: Yashin, Vasiliy, Drits, Alexander, Aryshenskii, Evgenii, Latushkin, Ilya, Chitnaeva, Ekaterina
Format: Article
Language:English
Subjects:
Aluminum base alloys
Deformation
Hot rolling
Ingot casting
Kinetics
Magnesium
Manganese
Optical microscopes
Recrystallization
Schedules
Zinc
Zirconium
Citations: Items that this one cites
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:The present study addresses recrystallization process in Al-Mg-Mn-Zn-Zr system alloy samples. The samples are collected from cast ingot, produced by casting to industrial DC mold, and homogenized based on standard industrial practice. After that the samples were rolled with different hot rolling schedules. Rolled samples were annealed at different temperatures and their resultant microstructure was examined using optical microscope. During the study new grains nuclei generation rate and their growth rate were determined, analytical records, describing recrystallization kinetics, were obtained, main differences, specific to this alloy recrystallization in 350 ºС-450 ºС temperature range, were identified.
ISSN:2261-236X
2274-7214
2261-236X
DOI:10.1051/matecconf/202032605001