Preparing Alumina-Supported Gold Nanowires for Alcohol Oxidation

• Published in: ACS omega 2021-06, Vol.6 (24), p.16043-16048
• Main Authors: Imura, Yoshiro, Maniwa, Motoki, Iida, Kazuki, Saito, Haruna, Morita-Imura, Clara, Kawai, Takeshi
• Format: Article
• Language: English
• ISSN: 2470-1343; 2470-1343
• DOI: 10.1021/acsomega.1c01895

The development of shape-controlled noble metal nanocrystals such as nanowires (NWs) is progressing steadily owing to their potentially novel catalytic properties and the ease with which they can be prepared by reducing the metal ions in a particular solution as capping agents. Recently, many reports have been presented on the preparation of shape-controlled Au nanocrystals, such as nanostars and nanoflowers, by a one-pot method using 2-[4-(2-hydroxyethyl)-1-piperazinyl] ethanesulfonic acid (HEPES) as capping and reducing agents. The catalytic activity is depressed due to the adsorption of the capping agent onto a Au surface. Since HEPES has low binding affinities on the Au surface, shape-controlled nanocrystals obtained using HEPES are effective for application as nanocatalysts because HEPES was easily removed from the Au surface. In this study, we report the preparation of AuNWs, with an average diameter of 7.7 nm and lengths of a few hundred nanometers, in an aqueous solution containing HEPES and sodium borohydride. A γ-Al2O3-supported AuNW (AuNW/γ-Al2O3) catalyst was obtained using catalytic supporters and a water extraction method that removed HEPES from the Au surface without morphological changes. AuNW/γ-Al2O3 was then utilized to catalyze the oxidation of 1-phenylethyl alcohol to acetophenone. The formation rate of acetophenone over AuNW/γ-Al2O3 was 3.2 times that over γ-Al2O3-supported spherical Au nanoparticles (AuNP/γ-Al2O3) with almost the same diameter.