Fatigue characterization of a crankshaft steel: Use and interaction of new models

The peculiar geometrical shape and working conditions of crankshafts make fatigue becoming responsible for most of the failure cases in such components. Therefore, improvement of crankshaft performance requires enhancing its fatigue life. In this work, the fatigue behavior of a D38MSV5S steel, used...

Full description

Saved in:
Bibliographic Details
Published in:Frattura ed integritá strutturale 2016-01, Vol.10 (35), p.187-195
Main Authors: Blasón, Sergio, Rodríguez, Cristina, Fernández-Canteli, Alfonso
Format: Article
Language:English
Subjects:
Crack growth rate curves
Crack propagation
Fatigue of crankshafts
Metal fatigue
Steel products
Citations: Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:The peculiar geometrical shape and working conditions of crankshafts make fatigue becoming responsible for most of the failure cases in such components. Therefore, improvement of crankshaft performance requires enhancing its fatigue life. In this work, the fatigue behavior of a D38MSV5S steel, used for crankshafts in compact vehicles, is investigated according to two traditional ways of analysis, namely the stress based and the fracture mechanics based approaches, though using advanced design models: On the one side, a probabilistic Weibull regression S-N model is assessed for experimental results obtained from fatigue resonance tests. On the other side, the crack growth rate curve is calculated from crack growth tests, carried out on SENB specimens, using a normalizing procedure. Specific Matlab programs are developed to facilitate the evaluation process. The information gained from both models will contribute to provide a probabilistic interpretation to the Kitagawa-Takahashi diagram.
ISSN:1971-8993
1971-8993
DOI:10.3221/IGF-ESIS.35.22