Collagen/Chitosan Functionalization of Complex 3D Structures Fabricated by Laser Direct Writing via Two-Photon Polymerization for Enhanced Osteogenesis

• Published in: International journal of molecular sciences 2020-09, Vol.21 (17), p.6426
• Main Authors: Păun, Irina Alexandra, Mustăciosu, Cosmin Cătălin, Popescu, Roxana Cristina, Călin, Bogdan Ştefăniţă, Mihăilescu, Mona
• Format: Article
• Language: English
• Subjects: 3D structure; Alizarin; Alkaline phosphatase; Biocompatibility; Biomedical materials; Blending effects; Bone biomaterials; Bones; Cell Differentiation; Cell Proliferation; Chitosan; Chitosan - chemistry; Collagen; Collagen - chemistry; collagen/chitosan functionalization; Direct laser writing; Gene expression; Glass substrates; Humans; laser direct writing; Lasers; Mineral deposits; Mixtures; Osteoblasts - cytology; Osteocalcin; Osteogenesis; Photons; Photopolymers; Polymerization; Polymers; Secretion; Solvents; Stem cells; Substitute bone; Surgical implants; Tissue engineering; Tissue Engineering - methods; Tissue Scaffolds - chemistry; Writing
• ISSN: 1422-0067; 1661-6596; 1422-0067
• DOI: 10.3390/ijms21176426

The fabrication of 3D microstructures is under continuous development for engineering bone substitutes. Collagen/chitosan (Col/CT) blends emerge as biomaterials that meet the mechanical and biological requirements associated with bone tissue. In this work, we optimize the osteogenic effect of 3D microstructures by their functionalization with Col/CT blends with different blending ratios. The structures were fabricated by laser direct writing via two-photons polymerization of IP-L780 photopolymer. They comprised of hexagonal and ellipsoidal units 80 µm in length, 40 µm in width and 14 µm height, separated by 20 µm pillars. Structures' functionalization was achieved via dip coating in Col/CT blends with specific blending ratios. The osteogenic role of Col/CT functionalization of the 3D structures was confirmed by biological assays concerning the expression of alkaline phosphatase (ALP) and osteocalcin secretion as osteogenic markers and Alizarin Red (AR) as dye for mineral deposits in osteoblast-like cells seeded on the structures. The structures having ellipsoidal units showed the best results, but the trends were similar for both ellipsoidal and hexagonal units. The strongest osteogenic effect was obtained for Col/CT blending ratio of 20/80, as demonstrated by the highest ALP activity, osteocalcin secretion and AR staining intensity in the seeded cells compared to all the other samples.