A long-term study on the effect of a hydrophobic treatment on the moisture balance and durability of a reinforced concrete structure in a road tunnel

Concrete structures in the vicinity of seawater or deicing salts on roads in regions with cold climatic conditions, are exposed to chlorides. Transport of chlorides in concrete due to capillary suction during drying and wetting cycles as well as diffusion in combination with carbonation tends to res...

Full description

Saved in:
Bibliographic Details
Published in:MATEC web of conferences 2022, Vol.364, p.4005
Main Authors: Brem, M., Lohner, J., Büchler, M.
Format: Article
Language:English
Subjects:
Carbonation
Chlorides
Concrete
Concrete structures
Corrosion mechanisms
Corrosion rate
Damage
Deicing salt
Durability
Embedded sensors
Hydrophobicity
Moisture effects
Rehabilitation
Reinforced concrete
Reinforcing steels
Seawater
Service life
Spraying
Structural integrity
Suction
Tunnels
Wetting
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Concrete structures in the vicinity of seawater or deicing salts on roads in regions with cold climatic conditions, are exposed to chlorides. Transport of chlorides in concrete due to capillary suction during drying and wetting cycles as well as diffusion in combination with carbonation tends to result in corrosion of the rebar and loss of structural integrity. This damage mechanism mainly applies to directly weathered components. After a longer service life, however, components that are not directly exposed, such as concrete surfaces outside the spraying water area of a tunnel, are also affected. A long-term study over 12 years was performed to investigate the effect of hydrophobic treatment on the moisture balance and durability of a suspended tunnel ceiling compared to an untreated surface with the same exposure. Embedded sensors installed in the concrete structure and an online monitoring system were used to measure the electrical resistivity of the concrete and the corrosion rate of the steel reinforcement over time. Furthermore, the data obtained were combined with climate measurements in the tunnel to gain new insights on the effect of tunnel climate on the damage mechanism. The measurements allowed to prove the long-term effect and correct application of hydrophobic treatment. With these results it is possible to make a more precise estimation of the condition and the deterioration process of the tunnel ceiling and to optimize the rehabilitation schedule.
ISSN:2261-236X
2274-7214
2261-236X
DOI:10.1051/matecconf/202236404005