Wear and mechanical characterization of Mg–Gr self-lubricating composite fabricated by mechanical alloying

• Published in: Journal of magnesium and alloys 2019-06, Vol.7 (2), p.283-290
• Main Authors: Al-maamari, Azzat Esam Abdulqader, Iqbal, AKM Asif, Nuruzzaman, Dewan Muhammad
• Format: Article
• Language: English
• Subjects: Characterization; Mechanical Alloying; Mechanical properties; Metal-matrix composites (MMCs); Wear
• ISSN: 2213-9567; 2213-9567
• DOI: 10.1016/j.jma.2019.04.002

In this research, the wear and mechanical responses of pure magnesium-graphite (Mg–Gr) composite have been investigated aiming to get the optimum composition of reinforcement. The composite materials were fabricated by mechanical alloying. The percentage of graphite reinforcement was chosen as 3, 5, 7 and 10 wt.% to identify its potential for self-lubricating property under dry sliding conditions. The mechanical properties including hardness, tensile strength and flexural strength of the composites and the base material were tested. The wear tests were conducted by using a pin-on-disc tribometer. The results show that the mechanical properties decrease with increasing graphite content as compared to that of the base material. The wear rate and average coefficient of friction decrease with the addition of graphite and was found to be minimum at 5 wt.% graphite reinforcement. The addition of 5 wt.% graphite in the composite exhibits superior wear properties as compared to that of the matrix material and other compositions of the Mg–Gr composites.