Point defects and hydrogen-permeation behavior of MAX phase Cr2AlC coating by first-principles studies

Because any fuel assembly material will be exposed to extensive irradiation during reactor operation, understanding the effects of irradiation on the microstructure of coatings and structural materials is critical to improving nuclear reactor safety and performance. In the present work, the point de...

Full description

Saved in:
Bibliographic Details
Published in:Nuclear materials and energy 2023-09, Vol.36, p.101486, Article 101486
Main Authors: Ling, Weidong, Lai, Kang, Chen, Jiahao, Guo, Fangyu, Kang, Dongdong, Zhao, Zengxiu, Dai, Jiayu
Format: Article
Language:English
Subjects:
Hydrogen diffusion
Irradiation damage
MAX-phase
Point defect
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Because any fuel assembly material will be exposed to extensive irradiation during reactor operation, understanding the effects of irradiation on the microstructure of coatings and structural materials is critical to improving nuclear reactor safety and performance. In the present work, the point defect and behavior of H in the MAX phase Cr2AlC coating are investigated using first-principles calculations. It is found that the electronic structure of MAX phase Cr2AlC material determines its special properties. The formation of Frenkel pairs leads to the expansion of interlayer spacing along the c-axis, which is the initial cause of the phase transition of the MAX phase structure caused by irradiation damage. Meanwhile, the relationship between the energy of intrinsic defect formation and the chemical potential was analyzed, which showed that sufficient C content was conducive to the structural stability of CrAl bonds. Additionally, the obtained a lower energy barrier of the H atom moving parallel to the Al plane, indicating that the H-bubble tends to aggregate near the Al atomic panel. This study provides a fundamental understanding of the point defect properties and the behavior of impurities in the MAX phase and provides theoretical support for the study of anti-radiation performance in nuclear applications. •The mechanism of irradiation-induced intrinsic defects.•Provides an atomistic insight to migration behaviors of impurity hydrogen atom in Cr2AlC film.•This work gives further proof of early investigation about irradiation induced structural transition.
ISSN:2352-1791
2352-1791
DOI:10.1016/j.nme.2023.101486