Morphological evolution of GP zones and nanometer-sized precipitates in the AA2050 aluminium alloy
Cs-corrected high-angle-annular-dark-field scanning-transmission-electron microscopy (Cs-corrected HAADF-STEM) was employed to examine the phases in AlCuLi alloy (AA2050), including GP(T1), GP(θ″) and GPB zones with their subsequent nanometer-sized products, T1 (Al2CuLi), θ′ (Al2Cu), and S (Al2CuMg)...
Saved in:
Published in: | International Journal of Lightweight Materials and Manufacture 2018-09, Vol.1 (3), p.142-156 |
---|---|
Main Authors: | , , , , , , , , , , |
Format: | Article |
Language: | English |
Subjects: | |
Citations: | Items that this one cites Items that cite this one |
Online Access: | Get full text |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Summary: | Cs-corrected high-angle-annular-dark-field scanning-transmission-electron microscopy (Cs-corrected HAADF-STEM) was employed to examine the phases in AlCuLi alloy (AA2050), including GP(T1), GP(θ″) and GPB zones with their subsequent nanometer-sized products, T1 (Al2CuLi), θ′ (Al2Cu), and S (Al2CuMg) precipitates, respectively. Under the peak-aging condition, some solute-atom enriched clusters could still be found, and the newly-formed nucleus of GP(θ″) with a mono-layer {100} plane of Cu atoms occurred at the adjacent area of the joint between θ′ and S precipitates or the edge of an individual S precipitate. The transition of a single Cu-layer GP(θ″) → θ′ was presumed to be transformation via in-situ nucleation. The developing GP(θ″) zones and θ′ precipitates were easily subjected to soft impingement. However, hard impingement between two variants of θ′ presumably occurred, wherein one θ′ variant precipitate was blocked out by the other θ′ variant. As for the creep-ageing forming (CAF) treated sample, some precipitates of T1 and θ′ were found to have the cutting characteristic on specific ledges. |
---|---|
ISSN: | 2588-8404 2588-8404 |
DOI: | 10.1016/j.ijlmm.2018.06.002 |