Structure and Optical Properties of Sn-Based Halide Perovskites (C10H18N2)SnX4 (X = Cl, Br, I)

• Published in: ACS omega 2024-05, Vol.9 (20), p.22352-22359
• Main Authors: Yao, Ruonan, Lin, Jiawei, Liu, Kunjie, Xu, Yuanchang, Xiao, Boyi, Zhao, Jing, Guo, Zhongnan, Liu, Quanlin, Yuan, Wenxia
• Format: Article
• Language: English
• ISSN: 2470-1343; 2470-1343
• DOI: 10.1021/acsomega.4c01835

Low-dimensional tin-based halide perovskites are considered as eco-friendly substitutions of the iconic lead-based perovskites to host the potential as optoelectronic materials. However, a fundamental understanding of the structure–property relationship of these Sn­(II)-based hybrids is still inadequate due to the limited members of this material family. To our knowledge, there is still lack of reports on a series of Sn­(II)-based halide perovskites with the same organic cation but covering chloride, bromide, and iodide. In this work, three new halide perovskites TMPDASnX4 (X = Cl, Br, I) (TMPDA = N,N,N′,N′-tetramethyl-1,4-phenylenediamine) are successfully synthesized, which provide the ideal paradigm to study the halogen-dependent evolution of the structure and properties of Sn­(II)-based hybrid perovskites. Despite sharing the same monoclinic lattice (P21/m space group), it is demonstrated that TMPDASnCl4 adopts a one-dimensional structure composed of a five-coordinated pyramid configuration due to an extremely long Sn···Cl distance, while the typical two-dimensional motif is still maintained in TMPDASnBr4 and TMPDASnI4. The ambient stability is declined in the order from chloride to bromide and then to iodide. TMPDASnCl4 exhibits a broad-band bluish-white-light emission (centered at 515 nm, full width at half-maximum (fwhm) = 193 nm) with the Commission Internationale de l′ Elairage (CIE) coordinates as (0.29, 0.34). Further, the correlated color temperature and color-rendering index were determined as 7617 K and 80.5, respectively. Based on the synthesis of new crystals, our work sheds light on the composition–structure–property relationship of hybrid Sn­(II)-based halide perovskites.