INORGANIC PHOSPHORS IN GLASS BASED ON LEAD SILICATE GLASSES

• Published in: Nauchno-tekhnicheskiĭ vestnik informat͡s︡ionnykh tekhnologiĭ, mekhaniki i optiki mekhaniki i optiki, 2014-09, Vol.14 (5), p.64-70
• Main Authors: V. A. Aseev, A. Y. Bibik, E. V. Kolobkova, Y. A. Nekrasova, N. V. Nikonorov, A. E. Romanov, J. V. Tuzova, M. A. Shvaleva
• Format: Article
• Language: English
• Subjects: lead silicate glass; luminescence spectra; luminous efficiency; phosphor in glass; white LEDs; yttrium-aluminum garnet doped with cerium
• ISSN: 2226-1494; 2500-0373

We created and synthesized luminescent composite of the "phosphor in glass" type, based on the lead-silicate matrix and fine-dispersed powder of cerium-activated yttrium-aluminum garnet crystal. Lead-silicate system (40SiO2- 20PbO-(40-x) PbF2-xAlF3, x = 0-25) was chosen as the glassy matrix. Initial glass was reduced to powder (frit) for "phosphor in glass" composite with a particle size about 50 µm. Glass frit and powder of commercial YAG:Ce3+ phosphor were mixed in a ratio of 30 to 70 (wt %). Then this composite was pressed in a tablet and sintered on a quartz substrate at 823 К for 30 minutes. Thus, the plane parallel sheet for composite of the "phosphor in glass" was obtained with a diameter equal to 10 mm. For the purpose to reduce the loss of light in the presence of dispersion at a glass-phosphor boundary, optimization of glass mixture was done by adjusting the refractive index. X-ray phase and spectral-luminescent analysis of the derived composite were done. The results of these studies showed that there was no degradation of YAG: Ce powder during sintering. Dependence of luminescence intensity from temperature in the range from room temperature to 473 К was studied. It was shown, that with the phosphor in glass usage thermal quenching of luminescence was reduced in comparison with the silicone. The model of white LED was created with the "phosphor in glass" composite based on lead-silicate glasses with low temperature of vitrifying. The derived LED emits white light with a color temperature of 4370 K, and the luminous efficiency is equal to 58 lm/W. The developed luminescent composite based on the lead-silicate matrix can be used for the production of high-power white light LED.