Prevention of hot cracking in Ni-based superalloy via passivation layer formation during additive manufacturing

We investigated the prevention of hot cracking in a non-weldable Ni-based superalloy by utilizing a passivation layer formed through laser-based directed energy deposition. The addition of Hf to the Ni-based superalloy facilitated the formation of a passivation layer consisting of Hf oxide on the su...

Full description

Saved in:
Bibliographic Details
Published in:Journal of materials research and technology 2024-11, Vol.33, p.3155-3162
Main Authors: Ryou, KenHee, Park, Yejun, Im, Hye Ji, Choi, Pyuck-Pa
Format: Article
Language:English
Subjects:
Additive manufacturing
Hot cracking
Ni-based superalloy
Passivation
Citations: Items that this one cites
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:We investigated the prevention of hot cracking in a non-weldable Ni-based superalloy by utilizing a passivation layer formed through laser-based directed energy deposition. The addition of Hf to the Ni-based superalloy facilitated the formation of a passivation layer consisting of Hf oxide on the surface of the as-deposited sample. An increase in the amount (thickness) of the passivation layers with increasing Hf content resulted in a reduction in hot cracking occurrence. Specifically, the addition of 2.5 wt% Hf led to the formation of uniformly distributed fine oxides without inducing hot cracks. This passivation layer effectively inhibited the formation of coarsened Mo oxides, which typically occur during oxidation in the liquid state and contribute to the hot cracking of Ni-based superalloy. During oxidation in the liquid state, Hf diffuses out to the surface and forms a passivation layer, thereby suppressing the formation and growth of oxides to sizes large enough to induce hot cracking.
ISSN:2238-7854
DOI:10.1016/j.jmrt.2024.09.251