Creation of special compositions based on butadiene-nitrile elastomers for diesels

• Published in: E3S web of conferences 2023-01, Vol.401, p.3028
• Main Authors: Mamayev, Sherali, Ibadullayev, Axmadjan, Nigmatova, Dilnoza, Teshabayeva, Elmira, Tursunaliev, Mukhsinjon
• Format: Article
• Language: English
• ISSN: 2267-1242; 2267-1242
• DOI: 10.1051/e3sconf/202340103028

In the article, it was determined that furan oligomer added to the composition causes additional structuring in the process of vulcanization, and as a result, the density and hardness of the vulcanization network in the composite increases, and the value of the relative length decreases. It was shown that the optimal amount of furan oligomers in the composition of rubber compounds is equal to 10 weight units per 100 weight units of rubber. With the inclusion of the secondary product of acetylene production in the elastomer compositions, it was found that the amount of carbon-rubber gel and the vulcanization network increased, and the level of vulcanizate shrinkage decreased, which was shown to be mainly due to the presence of oligomeric components on the surface of carbon particles. It is shown that the inclusion of this raw material in elastomeric compositions based on butadiene nitrile rubber increases the interaction at the “rubber-filler” boundary and the formation of additional bonds between rubber macromolecules and functional groups of the oligomer, and as a result, the overall technological and technical properties of the compositions are improved.