Influence of Boron on Crystallization and Microstructure of Ductile Cast Iron

The objective of the research was to determine the influence of boron on the crystallization process and microstructure of ductile cast iron. In the case of ductile cast iron it is a vital issue because even as little as trace presence of boron changes the properties of ductile cast iron in a signif...

Full description

Saved in:
Bibliographic Details
Published in:Archives of foundry engineering 2017-06, Vol.17 (2), p.15-20
Main Authors: Dojka, R., Studnicki, A.
Format: Article
Language:English
Subjects:
Boron
Ductile cast iron
Metallography
Solidification process
TDA
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:The objective of the research was to determine the influence of boron on the crystallization process and microstructure of ductile cast iron. In the case of ductile cast iron it is a vital issue because even as little as trace presence of boron changes the properties of ductile cast iron in a significant way. With the use of a new ATD-4 (TDA) tester and CRYSTALDIGRPAH converter it was possible to measure the crystallization process parameters of the same alloy with four different contents of boron in one mould. Four samples with different boron contents were extracted, their microhardness was measured and quantitative analysis of microstructure was conducted. Obtained results allowed to state that with increasing content of boron the amount of graphite precipitates decreases, the amount of pearlite precipitates increases, the shape of graphite precipitates deteriorates and hardness increases. It is also planned to perform additional testings with boron contents between previously tested values.
ISSN:2299-2944
2299-2944
DOI:10.1515/afe-2017-0043