The Effect of Preloading on Fatigue Damage in Composite Structures: Part 1

The effect of preload on damage development in unnotched graphite/epoxy laminates is studied. Two types of tension-tension fatigue tests were conducted on quasi-isotropic (0/45/-45/90)53, AS-4/3501-6 laminates, and damage was measured in the form of ply cracks. Baseline fatigue tests were run at con...

Full description

Saved in:
Bibliographic Details
Main Authors: Hahn, H. T, Timmer, Jeffrey L, Bartley-Cho, Johthan, Lee, Seaman, Lim, Seung-Gyu
Format: Report
Language:English
Subjects:
COMPOSITE STRUCTURES
COMPRESSION
COMPRESSIVE LOADS
CRACKING(FRACTURING)
DAMAGE ASSESSMENT
EPOXY LAMINATES
FATIGUE TESTS(MECHANICS)
FATIGUE(MECHANICS)
GRAPHITE EPOXY COMPOSITES
LAMINATES
Laminates and Composite Materials
MATRIX MATERIALS
Mechanics
RESIDUAL STRENGTH
STIFFNESS
STRENGTH(MECHANICS)
TENSILE STRENGTH
TENSILE STRESS
Online Access:Request full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:The effect of preload on damage development in unnotched graphite/epoxy laminates is studied. Two types of tension-tension fatigue tests were conducted on quasi-isotropic (0/45/-45/90)53, AS-4/3501-6 laminates, and damage was measured in the form of ply cracks. Baseline fatigue tests were run at constant amplitudes ranging from 20% to 60% of the ultimate tensile strength (UTS) while specimens with preloads of 50% to 80% UTS were tested in fatigue at the same amplitudes. The ply crack densities determined from edge replications in preloaded specimens were compared to those without preload. The effect of a preload on subsequent fatigue damage growth depended on the combination of both the preload level and the subsequent fatigue stress level. Since the tension preload was always higher than the tension-tension fatigue stress level, damage in preloaded specimens was more severe in the low-cycle region than nonpreloaded specimens. However, this preload-induced damage did not grow any more if the fatigue stress level was kept low. Preloads just above levels that cause significant damage (70% UTS and above here) appeared to retard fatigue damage development. At the highest tension-tension fatigue stress level of 40% UTS, the high-cycle damage in the form of matrix cracking rather decreased with increasing preload level. Thus, preloading could be beneficial at this stress level as far as the high-cycle ply crack damage is concerned.