The Crystallization Behavior of a Na[sub.2]O-GeO[sub.2]-P[sub.2]O[sub.5] Glass System: A Structural, Electrical, and Dielectric Study

• Published in: Materials 2024-01, Vol.17 (2)
• Main Authors: Marijan, Sara, Razum, Marta, Sklepić Kerhač, Kristina, Mošner, Petr, Koudelka, Ladislav, Pisk, Jana, Moguš-Milanković, Andrea, Skoko, Željko, Pavić, Luka
• Format: Article
• Language: English
• ISSN: 1996-1944; 1996-1944
• DOI: 10.3390/ma17020306

Sodium-phosphate-based glass-ceramics (GCs) are promising materials for a wide range of applications, including solid-state sodium-ion batteries, microelectronic packaging substrates, and humidity sensors. This study investigated the impact of 24 h heat-treatments (HT) at varying temperatures on Na-Ge-P glass, with a focus on (micro)structural, electrical, and dielectric properties of prepared GCs. Various techniques such as powder X-ray diffraction (PXRD), infrared spectroscopy-attenuated total reflection (IR-ATR), and scanning electron microscopy-energy dispersive spectroscopy (SEM-EDS) were employed. With the elevation of HT temperature, crystallinity progressively rose; at 450 °C, the microstructure retained amorphous traits featuring nanometric grains, whereas at 550 °C, HT resulted in fully crystallized structures characterized by square-shaped micron-scale grains of NaPO[sub.3]. The insight into the evaluation of electrical and dielectric properties was provided by Solid-State Impedance Spectroscopy (SS-IS), revealing a strong correlation with the conditions of controlled crystallization and observed (micro)structure. Compared to the initial glass, which showed DC conductivity (σ[sub.DC]) on the order of magnitude 10[sup.−7] Ω[sup.−1] cm[sup.−1] at 393 K, the obtained GCs exhibited a lower σ[sub.DC] ranging from 10[sup.−8] to 10[sup.−10] Ω[sup.−1] cm[sup.−1]. With the rise in HT temperature, σ[sub.DC] further decreased due to the crystallization of the NaPO[sub.3] phase, depleting the glass matrix of mobile Na[sup.+] ions. The prepared GCs showed improved dielectric parameters in comparison to the initial glass, with a noticeable increase in dielectric constant values (~20) followed by a decline in dielectric loss (~10[sup.−3]) values as the HT temperatures rise. Particularly, the GC obtained at @450 stood out as the optimal sample, showcasing an elevated dielectric constant and low dielectric loss value, along with moderate ionic conductivity. This research uncovers the intricate relationship between heat-treatment conditions and material properties, emphasizing that controlled crystallization allows for precise modifications to microstructure and phase composition within the remaining glassy phase, ultimately facilitating the fine-tuning of material properties.