Mechanical, Thermal, and Optical Properties of New Chloroantimonite Glasses in the Sb2O3–PbCl2 –Ag Cl System

• Published in: Materials science (New York, N.Y.) N.Y.), 2016-07, Vol.52 (1), p.33-41
• Main Authors: Yezli, D., Legouera, M., El Abdi, R., Poulain, M., Burgaud, V.
• Format: Article
• Language: English
• Subjects: Characterization and Evaluation of Materials; Chemistry and Materials Science; Diamond pyramid hardness; Materials Science; Mechanical properties; Modulus of elasticity; Optical properties; Physics; Refractivity; Solid Mechanics; Structural Materials; Thermodynamic properties
• ISSN: 1068-820X; 1573-885X
• DOI: 10.1007/s11003-016-9923-3

New chloroantimonite glasses were obtained in the Sb 2 O 3 – PbCl 2 –AgCl ternary system. Their thermal, optical, and mechanical properties are studied. The concentration of silver chloride increases at the expense of antimony oxide accordingtothe following composition rules: (80– x )Sb 2 O 3 –20PbCl 2 – x AgCl and (70– x )Sb 2 O 3 –30PbCl 2 – x AgCl. Depending on the AgCl content, Vickers microhardness varied between 110 MPa and 140 MPa. The elastic moduli were measured by ultrasonic velocity. The optical transmission range extended from 400 nm in the visible spectrum to 7 μm in the infrared spectrum. The refractive index was close to 2. The glass transition temperature measured by the DSC ranged from 250 to 290°C. It is shown that the glass transition temperature decreases as AgCl substitutes for Sb 2 O 3 and a more stable system was with 20% PbCl 2 in the (80– x )Sb 2 O 3 –20PbCl 2 – x AgCl.