Compressive performance and crack propagation in Al alloy/Ti2AlC composites

Composite materials comprising a porous Ti2AlC matrix and Al 6061 alloy were fabricated by a current-activated pressure assisted melt infiltration process. Coarse, medium and fine meso-structures were prepared with Al alloy filled pores of differing sizes. Materials were subjected to uniaxial compre...

Full description

Saved in:
Bibliographic Details
Published in:Materials science & engineering. A, Structural materials : properties, microstructure and processing Structural materials : properties, microstructure and processing, 2016-08, Vol.672, p.247-256
Main Authors: Hanaor, D.A.H., Hu, L., Kan, W.H., Proust, G., Foley, M., Karaman, I., Radovic, M.
Format: Article
Language:English
Subjects:
Aluminum base alloys
Civil Engineering
Compressive strength
Crack propagation
Cracks
Engineering Sciences
Fracture mechanics
Materials
Materials and structures in mechanics
Matériaux composites et construction
MAX phase
Mechanics
Mechanics of materials
Phases
Porosity
Shrinkage
Ti2AlC
Tomography, Crack propagation
XRM
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Composite materials comprising a porous Ti2AlC matrix and Al 6061 alloy were fabricated by a current-activated pressure assisted melt infiltration process. Coarse, medium and fine meso-structures were prepared with Al alloy filled pores of differing sizes. Materials were subjected to uniaxial compressive loading up to stresses of 668 MPa, leading to the failure of specimens through crack propagation in both phases. As-fabricated and post-failure specimens were analysed by X-ray microscopy and electron microscopy. Quasi-static mechanical testing results revealed that compressive strength was the highest in the fine structured composite materials. While the coarse structured specimens exhibited a compressive strength of 80% relative to this. Reconstructed micro-scale X-ray tomography data revealed different crack propagation mechanisms. Large planar shear cracks propagated throughout the fine structured materials while the coarser specimens exhibited networks of branching cracks propagating preferentially along Al alloy-Ti2AlC phase interfaces and through shrinkage pores in the Al alloy phase. Results suggest that control of porosity, compensation for Al alloy shrinkage and enhancement of the Al alloy-Ti2AlC phase interfaces are key considerations in the design of high performance metal/Ti2AlC phase composites.
ISSN:0921-5093
1873-4936
DOI:10.1016/j.msea.2016.06.073