High-field superconducting critical values of titanium bronze multifilamentary Nb3Sn conductors

• Published in: IEEE transactions on magnetics 1987-03, Vol.23 (2), p.637-640
• Main Authors: Kamata, K., Moriai, H., Tada, N., Watanabe, K., Nagata, A., Noto, K.
• Format: Article
• Language: English
• Subjects: Applied sciences; Conductors; Copper; Exact sciences and technology; Magnetic cores; Multifilamentary superconductors; Niobium; Niobium-tin; Other techniques and industries; Superconducting cables; Superconducting magnets; Titanium; Wires
• ISSN: 0018-9464; 1941-0069
• DOI: 10.1109/TMAG.1987.1064968

Multifilamentary Nb/Cu-7.5at%Sn-0.4at%Ti wires with two kinds of configurations were fabricated and their superconducting properties were evaluated. One kind of wires contain 1 \sim 5 \mu m-diam 31 × 361-Nb cores. These wires composed of our typical configuration with each 361-Nb cores embedded in a Cu-7.5Sn-0.4Ti matrix inside a Nb barrier, surrounded by a stabilizing Cu. The other kind of wire contains 4.7μm-diam 721-Nb cores in a Cu-7.5Sn-0.4Ti matrix inside a Nb barrier surrounded by a stabilizing Cu. The latter wire showed higher J c (overall) than the wire with the former configuration of about the same core diameter. The J c (overall) at 15 T exceeded 400 A/mm 2 at 4.2 K and reached to 570 A/mm 2 at 1.8 K for the latter wire heat treated at 650°C for 200 hr. While the 4.6μm-diam core wire with the former configuration showed a J c (overall) of 350 A/mm 2 at 15 T, 4.2 K after the heat treatment at 660°C for 200 hr, it also reached to 400 A/mm 2 at 15 T, 4.2 K when the core diameter was reduced to 2.7μm and heat treated at comparatively low temperature of 640°C for 200 hr. The H c 2's at 4.2 K were extrapolated to about 25 T for both kinds of wires. Since the T c 's were measured to be 16.8 K for these two kinds of wires, this H c 2 enhancement may be attributed to the ρn increase as a result of Ti incorporation into the Nb 3 Sn layer in the same way as that for Nb-Ti core Nb 3 Sn wires.