Magnetic properties and microstructure of Fe/FePt films with perpendicular magnetization

The soft/hard Fe/FePt bilayer with perpendicular magnetization has been prepared successfully on glass substrate. The (001) oriented L1 0 FePt film with fix thickness 10 nm was deposited on glass and subsequently annealing by rapid thermal process (RTP) at 800°C for 5 minutes and a Fe layer was depo...

Full description

Saved in:
Bibliographic Details
Main Authors: Jai-Lin Tsai, Hsin-Te Tzeng, Bing-Fong Liu
Format: Conference Proceeding
Language:English
Subjects:
Coercive force
Glass
Iron
Magnetic films
Magnetic hysteresis
Magnetic properties
Magnetization
Microstructure
Remanence
Soft magnetic materials
Online Access:Request full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:The soft/hard Fe/FePt bilayer with perpendicular magnetization has been prepared successfully on glass substrate. The (001) oriented L1 0 FePt film with fix thickness 10 nm was deposited on glass and subsequently annealing by rapid thermal process (RTP) at 800°C for 5 minutes and a Fe layer was deposited at room temperature with thickness of 2 nm to 10 nm. The control of Fe layer thickness allowed modifying the hysteresis loops from rigid magnet to exchange-spring magnet due to the nanoscale soft/hard interface coupling. When the Fe layer thickness increased to 3 nm, the out-of-plane coercivity is reduced to 5.88 kOe but the remanence ratio (0.98) is high. The Fe (3 nm)/FePt bilayer shows perpendicular magnetization with linear in-plane hysteresis loop. The remanence ratio is reduced to 0.86 when the Fe layer thickness increased up to 6 nm. When the Fe layer increased up to 10 nm, the hysteresis loop shows exchange spring-like behavior. The out-of-plane coercivity is still 4 kOe but the remanence ratio is 0.19. The films with perpendicular coercivity were moderated successfully by the soft magnetic layer with different thickness.
ISSN:2159-3523
DOI:10.1109/INEC.2010.5424945