The Structural and Electrical Properties of the Au/n-Si (MS) Diodes With Nanocomposites Interlayer (Ag-Doped ZnO/PVP) by Using the Simple Ultrasound-Assisted Method

• Published in: IEEE transactions on electron devices 2019-07, Vol.66 (7), p.3103-3109
• Main Authors: Altindal, S., Sevgili, O., Azizian-Kalandaragh, Y.
• Format: Article
• Language: English
• Subjects: <italic xmlns:ali="http://www.niso.org/schemas/ali/1.0/" xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink" xmlns:xsi="http://www.w3.org/2001/XMLSchema-instance">G /<italic xmlns:ali="http://www.niso.org/schemas/ali/1.0/" xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink" xmlns:xsi="http://www.w3.org/2001/XMLSchema-instance">ω –<italic xmlns:ali="http://www.niso.org/schemas/ali/1.0/" xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink" xmlns:xsi="http://www.w3.org/2001/XMLSchema-instance">V measurements; [Ag-ZnO/ polyvinylpyrrolidone (PVP)] nanocomposites; Bias; capacitance-voltage (<italic xmlns:ali="http://www.niso.org/schemas/ali/1.0/" xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink" xmlns:xsi="http://www.w3.org/2001/XMLSchema-instance">C –<italic xmlns:ali="http://www.niso.org/schemas/ali/1.0/" xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink" xmlns:xsi="http://www.w3.org/2001/XMLSchema-instance">V ); Crystallites; current-voltage (<italic xmlns:ali="http://www.niso.org/schemas/ali/1.0/" xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink" xmlns:xsi="http://www.w3.org/2001/XMLSchema-instance">I –<italic xmlns:ali="http://www.niso.org/schemas/ali/1.0/" xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink" xmlns:xsi="http://www.w3.org/2001/XMLSchema-instance">V ); Depletion; Electric potential; Electrical properties; Gold; II-VI semiconductor materials; Interlayers; Mathematical analysis; Nanocomposites; Nanocrystals; Nanoparticles; Nanostructures; Pattern analysis; Polymers; Scanning electron microscopy; Schottky diodes; Silver; structural and electrical properties; Thermionic emission; Ultrasonic methods; Ultrasonic testing; X-ray diffraction; X-ray scattering; Zinc oxide
• ISSN: 0018-9383; 1557-9646
• DOI: 10.1109/TED.2019.2913906

In this paper, Au/Ag-doped ZnO/polyvinyl pyrrolidone (PVP)/n-Si [metal-polymer-semiconductor (MPS)] Schottky Barrier Diodes (SBDs) were fabricated. The structural properties of the Ag-doped ZnO/PVP nanocomposites have been investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), and energy dispersive X-ray (EDX) analyses. The XRD pattern indicated that the samples have high purity ZnO and Ag materials and have not observed other peaks. The mean crystallite size of nanoparticles was calculated using Debye-Scherer's equation and the measured sizes reveal clearly the formation of small nanocrystals. The SEM and EDX results show the sheetlike ZnO nanostructures and also confirm the presence of Zn, O, and Ag materials with the nonstoichiometric ratio. The values of ideality factor ( {n} ), zero-bias barrier height ( \Phi _{B0} ), and series resistance ( {R}_{S} ) of the MPS-type SBD were obtained from both the thermionic emission (TE) and Cheung function and the observed some discrepancy between them was due to the voltage-dependent of these parameters and the nature of the calculation method. The value of surface states ( {N}_{\text {ss}} ) was changed from {2.2} \times {10}^{13} eV −1 cm −2 at ( {E} _{c} - {0.44} ) eV to {8.19} \times {10}^{12} eV −1 cm −2 at ( {E} _{c} - {0.69} ) eV and these values are more suitable for the MPS-type SBD. The values of doping-donor atoms ( {N} _{D} ), depletion layer width ( {W}_{D} ), and \Phi _{B} [capacitance-voltage ( {C} - {V} )] were obtained from the reverse bias