Structure and colossal dielectric permittivity of Ca2TiCrO6 ceramics

• Published in: Journal of physics. D, Applied physics Applied physics, 2013-01, Vol.46 (1)
• Main Authors: Yan-Qing, Tan, Meng, Yan, Yong-Mei, Hao
• Format: Article
• Language: English
• Subjects: Condensed matter: electronic structure, electrical, magnetic, and optical properties; Dielectric loss and relaxation; Dielectric properties of solids and liquids; Dielectrics, piezoelectrics, and ferroelectrics and their properties; Exact sciences and technology; Permittivity (dielectric function); Physics
• ISSN: 0022-3727; 1361-6463
• DOI: 10.1088/0022-3727/46/1/015303

A colossal permittivity ceramic material, Ca2TiCrO6, was successfully synthesized by the conventional solid-state reaction, and was characterized by scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), x-ray photoemission spectroscopy (XPS) and x-ray diffraction (XRD). Rietveld refinement of XRD data indicated that the material crystallized in orthorhombic structure with space group pbnm. SEM displayed Ca2TiCrO6 ceramic grains packed uniformly with the size range 5-20 µm. XPS analyses indicated that elemental chromium and titanium of the material were in mixed valence. The corresponding dielectric property was tested in the frequency range 1 kHz-1 MHz and the temperature range 213-453 K, and the ceramics exhibited a relaxation-like dielectric behaviour. Importantly, the permittivity of Ca2TiCrO6 could reach 80 000 at 298 K (100 Hz) and was maintained at 40 000 up to 398 K at 1 MHz, which could be attributed to the ion disorder and mixed valence of Cr3+/Cr6+ and Ti3+/Ti4+.