Hot corrosion studies on fully austenitic stainless steel in air oxidation and simulated waste heat incinerator environment at 600 °C, 650 °C and 700 °C

The purpose of the current study is to compare the hot corrosion performance of SMO 254 exposed to air oxidation and molten salt with a eutectic mixture of 40 wt% Na2SO4 + 40 wt% K2SO4 + 10 wt% NaCl + 10 wt% KCl at 600 °C, 650 °C and 700 °C under cyclic conditions for 50 h period. Kinetics of corros...

Full description

Saved in:
Bibliographic Details
Published in:Materials research express 2020-01, Vol.6 (12), p.1265
Main Authors: Roshith, P, Arivarasu, M
Format: Article
Language:English
Subjects:
air oxidation
hot corrosion
molten salt hot corrosion
thermogravimetric chart
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:The purpose of the current study is to compare the hot corrosion performance of SMO 254 exposed to air oxidation and molten salt with a eutectic mixture of 40 wt% Na2SO4 + 40 wt% K2SO4 + 10 wt% NaCl + 10 wt% KCl at 600 °C, 650 °C and 700 °C under cyclic conditions for 50 h period. Kinetics of corrosion were analyzed by thermogravimetric method. By using SEM/EDS, the hot corroded specimens were investigated for surface scales and cross-sectional elemental analysis by point, line mapping methods. An accelerated rate of corrosion rate was noticed in the specimen exposed to molten salt at 700 °C, and the lowest rate of corrosion rate was observed in the specimen subjected to air oxidation at 600 °C. XRD analysis is done to analyze the corrosion products in the oxide scale.
ISSN:2053-1591
2053-1591
DOI:10.1088/2053-1591/ab61ab