Effect of Nanosilica on the Mechanical and Thermal Properties of Carbon Fiber/Polycarbonate Laminates

• Published in: Fibers and polymers 2019, 20(8), , pp.1684-1689
• Main Authors: Fathalian, M., Ghorbanzadeh Ahangari, M., Fereidoon, A.
• Format: Article
• Language: English
• Subjects: Carbon fiber reinforced plastics; Carbon fibers; Chemistry; Chemistry and Materials Science; Differential scanning calorimetry; Glass transition temperature; Gravimetric analysis; Hydraulic presses; Laminates; Mechanical properties; Modulus of elasticity; Nanocomposites; Polycarbonate resins; Polymer Sciences; Silicon dioxide; Tensile tests; Thermal degradation; Thermal stability; Thermodynamic properties; Yield stress; 섬유공학
• ISSN: 1229-9197; 1875-0052
• DOI: 10.1007/s12221-019-1158-0

An investigation of nanosilica (SiO 2 ), influencing the mechanical and thermal attributes of carbon fiber (CF)/polycarbonate (PC) laminates, is described in this study. Polycarbonates with four different weight percentages of SiO 2 (PC-SiO 2 , 0.1, 0.3, 0.6 and 1.0 wt%) were prepared using a melt-blending technique. The PC-SiO 2 nanocomposites were then used to fabricate planar CF/PC laminates through a hot hydraulic press machine. The prepared laminates were characterized by a number of different techniques; namely, tensile tests, dynamic mechanical thermal analysis (DMTA), differential scanning calorimetry (DSC), thermal gravimetric analysis (TGA) and scanning electron microscopy (SEM). The tensile test findings revealed that when 0.6 wt% of SiO 2 was added to the laminate layers, the maximum tensile modulus and yield stress were achieved. The mechanical properties obtained by DMTA supported the tensile test results. It should be noted that the 0.6 wt% of SiO 2 had the highest mechanical properties. The DMTA and DSC analyses were used to measure the glass transition temperatures ( T g ) of laminates. We found that with the addition 0.6 wt% of SiO 2 the T g increased to approximately 1°C compared to 0 °C for the neat CF/PC laminate, meaning that by adding up 0.1 to 0.6 nanosilica to the polymer, the value T g first increased and then decreased. To characterize the mass loss, the thermal degradation of polycarbonate influenced by nitrogen was investigated through TGA. According to our TGA results, the highest thermal stability was achieved by adding 0.6 wt% of SiO 2 to the PC.