Corrosion resistance of alumina-forming alloys against molten chlorides for energy production. I: Pre-oxidation treatment and isothermal corrosion tests

• Published in: Solar energy materials and solar cells 2017-07, Vol.166 (C), p.222-233
• Main Authors: Gomez-Vidal, J.C., Fernandez, A.G., Tirawat, R., Turchi, C., Huddleston, W.
• Format: Article
• Language: English
• Subjects: Alloys; Alumina; Alumina-forming alloys; Aluminum; Aluminum alloys; Aluminum oxide; Catalytic oxidation; Chemical attack; Chemical degradation; Chloride; Chloride resistance; Chlorides; Corrosion; Corrosion products; Corrosion rate; Corrosion resistance; Corrosion resistant alloys; Corrosion tests; Electrochemistry; Forming; MATERIALS SCIENCE; Micrometers; Mitigation; Molten salts; Nickel base alloys; Oxidation; Oxides; Passivity; Potassium chloride; Salts; Scale (corrosion); SOLAR ENERGY; Solar power; Studies; Superalloys; Vapor phases
• ISSN: 0927-0248; 1879-3398
• DOI: 10.1016/j.solmat.2017.02.019

Advanced components in next-generation concentrating solar power (CSP) applications will require advanced heat-transfer fluids and thermal-storage materials that work from about 550°C to at least 720°C, for integration with advanced power-conversion systems. To reach the cost target, less-expensive salts such as molten chlorides have been identified as high-temperature fluid candidates. High-strength alloys need to be identified and their mechanical and chemical degradation must be minimized to be used in CSP applications. Approaches for corrosion mitigation need to be investigated and optimized to drive down corrosion rates to acceptable levels—in the order of tens of micrometers per year—for achieving a long system lifetime of at least 30 years. Surface passivation is a good corrosion mitigation approach because the alloy could then be exposed to both the liquid and the vapor phases of the salt mixture. In this investigation, we pre-oxidized the alumina-forming alloys Inconel 702, Haynes 224, and Kanthal APMT at different temperatures, dwelling times, and atmospheres to produce the passivation by forming protective oxides at the surface. The pretreated alloys were later corroded in molten MgCl2 – 64.41wt% KCl at 700°C in a flowing Ar atmosphere. We performed electrochemical techniques such as open-circuit potential followed by a potentiodynamic polarization sweep and conventional long-term weight-change tests to down-select the best-performing alloy and pre-oxidation conditions. The best corrosion results were obtained for In702 pre-oxidized in zero air at 1050°C for 4h. Metallographic characterization of the pre-oxidized alloys and of the corroded surfaces showed that the formation of dense and uniform alumina scale during the pre-oxidation appears to protect the alloy from attack by molten chloride. •Surface passivation was evaluated as a corrosion passivation approach.•Pre-oxidation was used to form protective oxides.•In702 (zero air, 1050°C, 4h) provided good corrosion resistance.•Dense/uniform alumina could be protecting the alloy from molten chloride attack.