Investigations of Polymethacrylate Tribochemical Films Using X-Ray Spectroscopy and Optical Profilometry

• Published in: Tribology letters 2021-03, Vol.69 (1), Article 26
• Main Authors: Erck, Robert A., Song, Miao, Li, Dongsheng, Cosimbescu, Lelia
• Format: Article
• Language: English
• Subjects: Chain transfer; Chemical composition; Chemistry and Materials Science; Copolymers; Corrosion and Coatings; Imidazole; INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CHEMISTRY; Ion beams; Materials Science; Microscopes; Microscopy; Monomers; Nanotechnology; optical imaging; Optical microscopy; organic tribochemical film; Original Paper; Oxygen enrichment; Physical Chemistry; Polymers; Polymethacrylates; Prepolymers; scanning electron microscopy; Substrates; Surfaces and Interfaces; Theoretical and Applied Mechanics; Thickness; Thin Films; Transmission electron microscopy; Tribology; wear
• ISSN: 1023-8883; 1573-2711
• DOI: 10.1007/s11249-020-01388-5

This study investigates the elemental composition and surface morphology of solid tribochemical films formed on steel surfaces. The reversible addition-fragmentation chain transfer (RAFT) method was used to synthesize nine different metal-free polymers, which were blended into commercial base oils. The polymers were either homopolymers of dodecyl methacrylate and ethylhexyl methacrylate or were co-polymers of these monomers with six polar monomers. After tribological testing at 100 °C using the ball-on-flat geometry, the resulting tribochemical films were imaged using scanning electron microscopy (SEM) and optical microscopy. The resulting tribochemical films have thicknesses around 50–100 nm. Two of the films corresponding to small ( P1 —imidazole-containing copolymer) and large ( P3 —less polar homopolymer) wear were cross-sectioned using focused ion beam (FIB) and analyzed for elemental composition using energy-dispersive X-Ray (EDX) mapping. Oxygen and nitrogen enrichment was observed, consistent with the relative chemical composition of the precursor polymers. Transmission electron microscopy (TEM) evidence suggests that at the worn surface, some organic elements penetrate or are mixed into the steel substrate giving an interlocking appearance. The two samples examined with TEM showed that P1 tribofilm is diffused or mixed with the steel substrate more so than P3 , suggesting a stronger affinity and contact during tribofilm formation. Graphic Abstract