Dissolution of calcium-deficient hydroxyapatite synthesized at different conditions
The dissolution characteristics of several calcium-deficient hydroxyapatites (HA) have been investigated. Eleven samples were produced by varying synthesis parameters like temperature, pH, digestion time, reagent concentration and velocity of addition. Powder characterization was conducted using X-r...
Saved in:
Published in: | Materials characterization 2003-03, Vol.50 (2), p.203-207 |
---|---|
Main Authors: | , , , , , |
Format: | Article |
Language: | English |
Subjects: | |
Citations: | Items that this one cites Items that cite this one |
Online Access: | Get full text |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Summary: | The dissolution characteristics of several calcium-deficient hydroxyapatites (HA) have been investigated. Eleven samples were produced by varying synthesis parameters like temperature, pH, digestion time, reagent concentration and velocity of addition. Powder characterization was conducted using X-ray diffraction. Sample crystallinity was variable and samples examined by transmission electron microscopy showed acicular or plate-like morphology. After sample dissolution in Milli-Q water for 168 h, the calcium and phosphate contents in solution were measured by induced coupled plasma optical emission spectrometry (OES). The dissolution behavior of calcium-deficient HA was highly dependent on the sample calcium/phosphorus (Ca/P) molar ratio of the original HA. Dissolution in water was enhanced with decreasing HA sample molar ratio. However, the dissolution process equilibrium was not achieved at the end of 168 h (7 days). |
---|---|
ISSN: | 1044-5803 1873-4189 |
DOI: | 10.1016/S1044-5803(03)00093-7 |