EXAFS Characterization of Dendrimer-Derived Pt/-Al2O3

The various steps involved in the preparation of a Pt/-Al2O3 material using hydroxyl-terminated generation four (G4OH) PAMAM dendrimers as templates were monitored by EXAFS. The results indicate that Cl ligands in the Pt precursors (H2PtCl6 and K2PtCl4) were partially replaced by aquo ligands upon h...

Full description

Saved in:
Bibliographic Details
Published in:AIP conference proceedings 2007-02, Vol.882 (1), p.737-739
Main Authors: Siani, A, Alexeev, O S, Williams, C T, Ploehn, H J, Amiridis, M D
Format: Article
Language:English
Subjects:
ABSORPTION SPECTROSCOPY
ALUMINIUM OXIDES
BOROHYDRIDES
CATALYSTS
ELECTRON DENSITY
ELECTRONIC STRUCTURE
FINE STRUCTURE
HEAT TREATMENTS
HYDROLYSIS
HYDROXIDES
INTERFACES
LIGANDS
MATERIALS SCIENCE
NANOSTRUCTURES
NITROGEN
PARTICLES
PLATINUM
REDUCTION
SINTERING
X-RAY SPECTROSCOPY
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:The various steps involved in the preparation of a Pt/-Al2O3 material using hydroxyl-terminated generation four (G4OH) PAMAM dendrimers as templates were monitored by EXAFS. The results indicate that Cl ligands in the Pt precursors (H2PtCl6 and K2PtCl4) were partially replaced by aquo ligands upon hydrolysis to form [PtCl3(H2O)3]+ and [PtCl2(H2O)2] species. After interaction of such species with G4OH, Cl ligands from the first coordination shell of Pt were further replaced by nitrogen atoms from the dendrimer interior, indicating the complexation of Pt with the dendrimer. This process was accompanied by a transfer of the electron density from the dendrimer to Pt, indicating that the former plays the role of a ligand. Following treatment of the H2PtCl6/G4OH and K2PtCl4/G4OH composites with NaBH4, no substantial changes were detecteded in the electronic or coordination environment of Pt, and no formation of metal nanoparticles was observed. However, when the reduction treatment was performed with H2, the formation of extremely small Pt clusters incorporating no more than 4 Pt atoms was observed. These Pt species remained strongly bonded to the dendrimer and their nuclearity depends on the length of the H2 treatment. Formation of Pt nanoparticles with an average diameter of approximately 10 A was finally observed after the deposition of H2PtCl6/G4OH on -Al2O3 and drying, suggesting that their formation may be related to the collapse of the dendrimer structure. The Pt nanoparticles formed appear to have high mobility, since subsequent thermal treatment in O2/H2 led to further sintering.
ISSN:0094-243X
1551-7616
DOI:10.1063/1.2644648