Growth temperature effect on the structural and magnetic properties of Fe{sub 3}O{sub 4} films grown by the self-template method

We have investigated the effect of growth temperature on the structure, surface morphology, and magnetic properties of Fe{sub 3}O{sub 4} thin films grown on SrTiO{sub 3}(001) substrates by a self-template method. To eliminate the intermixing of (001) and (111) orientations that usually occurs in spi...

Full description

Saved in:
Bibliographic Details
Published in:Journal of applied physics 2014-07, Vol.116 (3)
Main Authors: Takahashi, R., Misumi, H., Lippmaa, M.
Format: Article
Language:English
Subjects:
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:We have investigated the effect of growth temperature on the structure, surface morphology, and magnetic properties of Fe{sub 3}O{sub 4} thin films grown on SrTiO{sub 3}(001) substrates by a self-template method. To eliminate the intermixing of (001) and (111) orientations that usually occurs in spinel films grown on perovskite substrates, a thin self-template layer of (001)-oriented Fe{sub 3}O{sub 4} was deposited on a SrTiO{sub 3}(001) substrate at 400 °C prior to the main film growth at temperatures of up to 1100 °C. Increasing the growth temperature from 400 °C to 1100 °C resulted in greatly improved crystallinity of the Fe{sub 3}O{sub 4} thin films, with the rocking curve width dropping from 1.41° to 0.28°. Surface analysis by atomic force microscopy showed that raising the growth temperature increased the grain size and the surface roughness, ultimately leading to the formation of regular nanopyramid arrays at 1100 °C. The surface roughening and pyramid formation are caused by the dominance of the lowest surface energy spinel (111) crystal facet. The nanopyramids were fully relaxed but still perfectly (001)-oriented in the out-of-plane direction. The largest pyramids had the lowest coercivity due to a reduction of the demagnetization effect.