Probing the Behavior of Composition‐Tunable Ultrathin PtNi Nanowires for CO Oxidation and Small‐Molecule Electrocatalytic Reactions

Abstract We have successfully synthesized ultrathin nanowires of pure Pt, Pt 99 Ni 1 , Pt 9 Ni 1 , and Pt 7 Ni 3 using a modified room‐temperature soft‐template method. Analysis of both methanol oxidation reaction (MOR) and ethanol oxidation reaction (EOR) results found that the Pt 7 Ni 3 samples yi...

Full description

Saved in:
Bibliographic Details
Published in:ChemNanoMat : chemistry of nanomaterials for energy, biology and more biology and more, 2023-11, Vol.10 (2)
Main Authors: Hurley, Nathaniel, Gallagher, Michael, Koenigsmann, Christopher, Stephanie, Elena, Davoudi, Monireh, Plonka, Anna M., Wang, Haodong, Zhang, Lihua, Frenkel, Anatoly I., Wong, Stanislaus S.
Format: Article
Language:English
Subjects:
alloy formation
electrocatalysis
MATERIALS SCIENCE
nanowires
small molecule reactions
solution-based synthesis
XAS spectroscopy
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Abstract We have successfully synthesized ultrathin nanowires of pure Pt, Pt 99 Ni 1 , Pt 9 Ni 1 , and Pt 7 Ni 3 using a modified room‐temperature soft‐template method. Analysis of both methanol oxidation reaction (MOR) and ethanol oxidation reaction (EOR) results found that the Pt 7 Ni 3 samples yielded the best performance with specific activities of 0.36 and 0.34 mA/cm 2 respectively. Additionally, formic acid oxidation reaction (FAOR) tests noted that both Pt and PtNi nanowires oxidize small organic molecules (SOMs) via an indirect pathway. CO oxidation data suggests little measurable performance without any pre‐reduction treatment; however, after annealing in H 2 , we detected significantly improved CO 2 formation for both Pt 9 Ni 1 and Pt 7 Ni 3 motifs. These observations highlight the importance of pre‐treating these nanowires under a reducing atmosphere to enhance their performance for CO oxidation. To explain these findings, we collected extended x‐ray adsorption fine structure (EXAFS) spectroscopy data, consistent with the presence of partial alloying with a tendency for Pt and Ni to segregate, thereby implying the formation of a Pt‐rich shell coupled with a Ni‐rich core. We also observed that the degree of alloying within the nanowires increased after annealing in a reducing atmosphere, a finding deduced through analysis of the coordination numbers and calculations of Cowley's short range order parameters.