High Performance 2G Wires: From R&D to Pilot-Scale Manufacturing

• Published in: IEEE transactions on applied superconductivity 2009-06, Vol.19 (3), p.3225-3230
• Main Authors: Selvamanickam, V., Yimin Chen, Xuming Xiong, Xie, Y.Y., Martchevski, M., Rar, A., Yunfei Qiao, Schmidt, R.M., Knoll, A., Lenseth, K.P., Weber, C.S.
• Format: Article
• Language: English
• Subjects: Activation; Applied sciences; Buffers; BZO; cable; Chemical vapor deposition; Chemistry; Critical current; Devices; Electrical engineering. Electrical power engineering; Electrical power engineering; Electromagnets; Electronics; Exact sciences and technology; High temperature superconductors; IBAD; long length; Manufacturing; Microelectronic fabrication (materials and surfaces technology); Miscellaneous; MOCVD; Organic chemicals; Power networks and lines; second-generation HTS; Segments; Semiconductor electronics. Microelectronics. Optoelectronics. Solid state devices; Superconducting devices; Superconducting tapes; Surface layer; Texture; Various equipment and components; Wire; Wires; Yttrium barium copper oxide; Zirconium
• ISSN: 1051-8223; 1558-2515
• DOI: 10.1109/TASC.2009.2018792

Tremendous progress has been accomplished in 2008 in key metrics of YBa 2 Cu 3 O x (YBCO) second-generation (2G) HTS wires at SuperPower. Using improved precursor chemistry in our metal organic chemical vapor deposition (MOCVD) process, critical currents (I c ) as high as 813 A/cm were reached over meter-long lengths, representing the highest reported I c in meter long 2G HTS. By use of Zr doping of (Gd,Y)Ba 2 Cu 3 O x , strong enhancements were achieved in in-field performance over a wide angular range. A I c of 229 A/cm was achieved at 77 K and 1 T perpendicular to the wire which is about a factor of 2.5 times better than that of standard MOCVD-derived films. At 65 K and 3 T, a I c of 340 A/cm was demonstrated perpendicular to the wire. Kilometer lengths of 2G HTS have been demonstrated for the first time. Over 35 tapes 1,000 to 1,500 m in length with a complete 5-layer buffer stack have been routinely produced in our pilot-scale manufacturing facilities. An excellent in-plane texture of 6 to 7 degrees with a uniformity of about 2% was reproducibly achieved in the kilometer-long fully-buffered tapes. Using these high-quality buffers, the longest 2G wire length to date of 1,311 m was produced with a minimum Ic of 153 A/cm corresponding to a I c times length value of 200,580 m. Also, an 1,030 m long complete 2G HTS wire has been demonstrated with a minimum Ic of 227 A/cm corresponding to a record I c times length value of 233,810 A-m. Further, a 630 m long segment of the wire sustained a minimum I c of 302 A/cm, the longest 2G wire reported to date with a I c over 300 A/cm. Also, a I c of 337 A/cm was achieved over a 540 m long segment. All these values represent a 2 to 3 fold improvement in length and I c of 2G wires compared to our achievements in 2007. In 2008, a 30 m long 2G cable made with nearly 10,000 m of 2G wire previously delivered by SuperPower was successfully installed and energized in the grid of National Grid in downtown Albany, marking the world's first of 2G HTS device in the power grid.