Modified shape memory epoxy resin composites by blending activity polyurethane

A series of modified shape‐memory epoxy resin composites were prepared by blending activity polyurethane (APU). Fourier transform infrared spectroscopy (FTIR), tensile tests, scanning electron microscope (SEM), dynamic mechanical analysis (DMA), and fold‐deploy shape memory tests were used to charac...

Full description

Saved in:
Bibliographic Details
Published in:Journal of applied polymer science 2013-02, Vol.127 (4), p.3152-3158
Main Authors: Liu, Yuyan, Sun, He, Tan, Huifeng, Du, Xingwen
Format: Article
Language:English
Subjects:
activity polyurethane
Applied sciences
Chemical properties
Exact sciences and technology
Materials science
modified
Polymer industry, paints, wood
Polymers
Properties and testing
shape-memory polymer
Technology of polymers
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:A series of modified shape‐memory epoxy resin composites were prepared by blending activity polyurethane (APU). Fourier transform infrared spectroscopy (FTIR), tensile tests, scanning electron microscope (SEM), dynamic mechanical analysis (DMA), and fold‐deploy shape memory tests were used to characterize the structure, mechanical, morphology, thermodynamics, and shape memory performance of these materials. FTIR results suggest that APU has been introduced into the resin matrix resin. Tensile test results show that the addition of appropriate APU can increase the elongation at break significantly, compared with neat epoxy. SEM results indicate that the fracture mechanism has changed from brittle to ductile, suggesting that the brittleness of the material has been overcome. DMA results show that modified materials have lower glass transition temperature (Tg) and lower cross‐linking density for shape memory function. Furthermore, the fold‐deploy shape memory tests prove that the materials possess excellent shape memory properties. They can be deformed into different shapes and recover their original shapes fully within 2 min at Tg, while they are hardly affected by ninefold‐deploy cycles. © 2012 Wiley Periodicals, Inc. J. Appl. Polym. Sci., 2013
ISSN:0021-8995
1097-4628
DOI:10.1002/app.37688