Synthesis of Borohydride and Catalytic Dehydrogenation by Hydrogel Based Catalyst

• Published in: Journal of electronic materials 2016-08, Vol.45 (8), p.3949-3956
• Main Authors: Boynuegri, Tugba Akkas, Karabulut, Ahmet F., Guru, Metin
• Format: Article
• Language: English
• Subjects: Catalytic polymerization; Characterization and Evaluation of Materials; Chemical synthesis; Chemistry and Materials Science; Dehydrogenases; Electronics and Microelectronics; Hydrogels; Instrumentation; Materials Science; Optical and Electronic Materials; Solid State Physics
• ISSN: 0361-5235; 1543-186X
• DOI: 10.1007/s11664-016-4620-4

This paper deals with the synthesis of calcium borohydride (Ca(BH 4 ) 2 ) as hydrogen storage material. Calcium chloride salt (CaCl 2 ), magnesium hydride (MgH 2 ), and boron oxide (B 2 O 3 ) were used as reactants in the mechanochemical synthesis of Ca(BH 4 ) 2 . The mechanochemical reaction was carried out by means of Spex type ball milling without applying high pressure and temperature. Parametric studies have been established at different reaction times and for different amounts of reactants at a constant ball to powder ratio (BPR) 4:1. The best combination was determined by Fourier Transform Infrared (FT-IR) analysis. According to the FT-IR analysis, reaction time, the first reaction parameter, was found as 1600 min. After the reaction time was fixed at 1600 min, the difference of the B-H peak areas was dependent on the amount of reactant MgH 2 that was investigated. The amount of the reactant (MgH 2 ), the second reaction parameter, was measured to be 2.85 times more than the stoichiometric amount of MgH 2 . According to our previous studies, BPR was selected as 4:1 for all experiments. Samples were prepared in a glove box under argon atmosphere but the time that elapsed for FT-IR analysis highly affected B-H bonds. B-H peak areas clearly decreased with time because of negative effect of ambient atmosphere. A catalyst was prepared by absorbing cobalt fluoride (CoF 2 ) in poly (acrylamide-co-acrylic acid) hydrogel matrices type and its catalytic dehydrogenation performance that has been characterized by the catalytic reaction of sodium borohydride's known hydrogen capacity in an alkaline medium. The metal amount of hydrogel catalyst was determined as 135.82 mg Co by Atomic Absorption Spectroscopy (AAS). The specific dehydrogenation capacity of the Co active compound in the catalyst thanks to catalytic dehydrogenation of commercial sodium borohydride was measured as 1.66 mL H 2 /mg Co.