Tensile properties and microstructure of a cryomilled nanograined Al-Mg alloy near the AA5083 composition

• Published in: Materials science & engineering. A, Structural materials : properties, microstructure and processing Structural materials : properties, microstructure and processing, 2017-09, Vol.705, p.239-248
• Main Authors: Kaisar, K.H., Hofmeister, C., Pedigo, A., Giri, A.K., Sohn, Y., Cho, K.C., van den Bergh, M., Majumdar, B.S.
• Format: Article
• Language: English
• Subjects: AA5083; Alloy development; Aluminum alloys; Aluminum base alloys; Consolidation; Corrosion resistance; Corrosion resistant alloys; Cryomilling; Ductility; Elongation; Extrusion; Grain size; Liquid nitrogen; Magnesium; Microstructure; Multiscale; Nanocrystalline; Nanocrystals; Studies; Tensile properties; Tensile strength; Tensile tests; Ultimate tensile strength; Ultrafine grained
• ISSN: 0921-5093; 1873-4936
• DOI: 10.1016/j.msea.2017.08.073

In an effort to develop high strength aluminum alloys, a near-AA5083 Al-Mg alloy powder was cryomilled in liquid nitrogen and consolidated by vacuum hot-pressing (VHP). The composition of the Al-Mg alloy was designed to minimize intermetallic particles that often lead to premature fracture especially when flow strength is high. The as-VHP material had poor ductility and therefore was extruded under different conditions to obtain a good combination of tensile strength and ductility. The microstructure of samples were characterized using X-ray diffraction, EBSD, FIB induced secondary electron orientation contrast imaging, and TEM techniques, which together provided unique assessment at multiple length scales. The samples exhibited a wide range of grain sizes that could be binned into three different groups: i) grain sizes of 50–100nm, (ii) sizes in the 100–300nm range, and (iii) elongated larger grains with widths in the range 0.5–2µm. Room temperature tensile tests with cylindrical dog-bone geometry indicated a high ultimate strength of 730–770MPa and reproducible elongation to failure of about 3–4%. This combination of strength and ductility in the material are some of the best that have been reported for alloys close to the weldable and corrosion resistant AA5083 composition, and likely a result of the multi-scale microstructure resulting from the processing route.