MOF derived Mesoporous Nitrogen doped Carbons with high Activity towards Oxygen Reduction

[Display omitted] In order to obtain Platinum-free catalysts for the Oxygen Reduction Reaction (ORR) in Fuel Cells, Nitrogen doped mesoporous carbons were prepared from pyrolysis of three Cobalt metal organic frameworks (MOFs), one linear coordination polymer and one complex. Electron micrographs re...

Full description

Saved in:
Bibliographic Details
Published in:Electrochimica acta 2017-10, Vol.251, p.638-650
Main Authors: Díaz-Duran, Ana Katherine, Roncaroli, Federico
Format: Article
Language:English
Subjects:
Bars
Catalysis
Catalysts
Cobalt
Coordination compounds
coordination polymer
Coordination polymers
Electrokinetics
Electrolytes
Electron micrographs
Exchanging
fuel cell
Fuel cells
Hydrogen peroxide
metal organic framework
Metal-organic frameworks
Methanol
Nitrogen
non-noble catalyst
Photomicrographs
Platinum
Platinum-free
polymer electrolyte membrane
Polymers
Pyrolysis
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:[Display omitted] In order to obtain Platinum-free catalysts for the Oxygen Reduction Reaction (ORR) in Fuel Cells, Nitrogen doped mesoporous carbons were prepared from pyrolysis of three Cobalt metal organic frameworks (MOFs), one linear coordination polymer and one complex. Electron micrographs revealed the presence of pores of different sizes in the samples. Particles resembled polyhedrons, sponges, bars, etc. The catalyst derived from Cobalt 2,3-pyrazinedicarboxylate polymer (700°C) exhibited attractive electrokinetic parameters for the ORR comparable to those of Pt 20% in acidic medium (Tafel slope=82 mV dec−1, exchange current density=10mAcm−1, equilibrium potential=907 mV (vs RHE), half wave potential=720 mV (vs RHE), number of exchanged electrons ca. 4.0, 0.5 M H2SO4). Limiting current and H2O2 yield (< 10%) are similar to those of ZIF-67 derived materials. The half wave potential is shifted to 820 mv (vs RHE) in alkaline medium (0.1 M KOH). The former sample holds a surface area on mesopores which duplicates that of the ZIF-67 700°C. A correlation was found between the current intensity for the ORR and the mesopore area occupied by N (%N x specific area on mesopores). The Cobalt 2,3-pyrazinedicarboxylate derived material (700°C) showed high methanol tolerance compared to Pt 20% (0.05 M methanol, 0.5 M H2SO4), and good ORR durability (after 3000 cycles between 0.25–1.15 V vs RHE, O2 saturated 0.5M H2SO4).
ISSN:0013-4686
1873-3859
DOI:10.1016/j.electacta.2017.08.055