Analysis of the Coating for Heavy Liquid Metal Applications

This paper deals with the behavior of the ferritic-martensitic steel T91 samples covered with an AlTiN black coating, which is mainly used for high temperature applications (> 800 ° C) because of its resistance to oxidation. The coating was applied by use of a combination of High Power Impulse Ma...

Full description

Saved in:
Bibliographic Details
Published in:Korose a ochrana materiálu 2017-12, Vol.61 (5), p.173-177
Main Authors: Prehradná, J., Rozumová, L., Di Gabriele, F., Chocholoušek, M., Dostál, V.
Format: Article
Language:English
Subjects:
Callisto
Coating
Direct current
Ferritic stainless steels
Jupiter
Jupiter satellites
Magnetron sputtering
Martensitic stainless steels
Oxidation resistance
Citations: Items that this one cites
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:This paper deals with the behavior of the ferritic-martensitic steel T91 samples covered with an AlTiN black coating, which is mainly used for high temperature applications (> 800 ° C) because of its resistance to oxidation. The coating was applied by use of a combination of High Power Impulse Magnetron Sputtering (HiPIMS) and Direct Current Magnetron Sputtering (DCMS). Samples were subjected to a tensile test in a static tank CALLISTO. The environment was liquid PbBi eutectic at a temperature of 550° C. Two types of samples, with a notch in the middle and without a notch, were tested. After exposure, the samples were subjected to morphological and chemical analyzes on SEM and EDX. Although the coating cracked over the entire length of the sample, high adhesion of the layer was demonstrated, the coating was delaminated locally only in the notch.
ISSN:1804-1213
0452-599X
1804-1213
DOI:10.1515/kom-2017-0022