Synergistic flame retardant effects of activated carbon and molybdenum oxide in poly(vinyl chloride)

The synergistic effects of activated carbon (AC) and molybdenum oxide (MoO3) in improving the flame retardancy of poly(vinyl chloride) (PVC) were investigated. The effects of AC, MoO3 and their mixture with a mass ratio of 1:1 on the flame retardancy and smoke suppression properties of PVC were stud...

Full description

Saved in:
Bibliographic Details
Published in:Polymer international 2018-04, Vol.67 (4), p.445-452
Main Authors: Zhang, Mengjiao, Wu, Weihong, He, Shaorui, Wang, Xue, Jiao, Yunhong, Qu, Hongqiang, Xu, Jianzhong
Format: Article
Language:English
Subjects:
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:The synergistic effects of activated carbon (AC) and molybdenum oxide (MoO3) in improving the flame retardancy of poly(vinyl chloride) (PVC) were investigated. The effects of AC, MoO3 and their mixture with a mass ratio of 1:1 on the flame retardancy and smoke suppression properties of PVC were studied using the limiting oxygen index and cone calorimeter tests. It was found that the flame retardancy of the relatively cheaper AC was slightly weaker than that of MoO3. In addition, the incorporation of AC and MoO3 greatly reduced the total heat release and improved smoke suppressant property of PVC composites. When the total content of AC and MoO3 was 10 phr, PVC/AC/MoO3 had the lowest peak heat release rate and peak smoke production rate values of 173.80 kW m−2 and 0.1472 m2 s−1, which represented reductions of 47.3 and 59.9%, respectively, compared with those of PVC. Furthermore, thermogravimetric analysis and gel content tests were used to analyze the flame retardant mechanism of AC and MoO3, with results showing that AC could promote early crosslinking in PVC. Char residue left after heating at 500 °C was analyzed using scanning electron microscopy and Raman spectroscopy, and the results showed that MoO3 produced the most compact char, with the smallest and most organized carbonaceous microstructures. © 2017 Society of Chemical Industry Activated carbon (AC) and MoO3 can effectively promote the crosslinking carbonization reaction of poly(vinyl chloride) (PVC) in different degradation stages, and therefore the PVC/AC/MoO3 composite has the best flame retardant and smoke suppression properties.
ISSN:0959-8103
1097-0126
DOI:10.1002/pi.5526