Controlling liquid segregation of semi-solid AZ80 magnesium alloy by back pressure thixoextruding

• Published in: Journal of materials processing technology 2018-09, Vol.259, p.88-95
• Main Authors: Chen, Gang, Zhang, Shun, Zhang, Hongming, Han, Fei, Wang, Gang, Chen, Qiang, Zhao, Zude
• Format: Article
• Language: English
• Subjects: Alloys; Aluminum alloys; Atoms & subatomic particles; Back pressure; Elastic deformation; Liquid segregation; Magnesium alloys; Magnesium base alloys; Mechanical properties; Melting; Microstructure; Rheology; Semisolids; Springs (elastic); Stress concentration; Surface properties; Thixoforming
• ISSN: 0924-0136; 1873-4774
• DOI: 10.1016/j.jmatprotec.2018.04.023

A back pressure thixoextruding method was proposed to control the liquid segregation during the thixoforming process. The back pressure was provided by disk springs which can apply an elastic force on the deformed alloy to make it in a three-dimensional compression stress state. Thixoextrusion of AZ80 magnesium alloy was conducted to verify the feasibility of the proposed technology. The results show that the suitable partial remelting regime for AZ80 magnesium alloy is isothermal holding at 560 °C for 15–25 min. Although the components with good surface qualities can be successfully fabricated by both back pressure thixoextruding and conventional thixoextruding, the distribution of microstructures and mechanical properties are quite different. Severe liquid segregation occurred during the conventional thixoextruding process, and a great amount of liquid-solidified structures were detected in the peripheral area, resulting in lower mechanical properties. By applying a back pressure in the thixoextruding process, the liquid segregation was reduced effectively, and the microstructures and mechanical properties are homogeneous among different positions. Back pressure thixoextruding is an efficient method for controlling the liquid segregation behavior and has great potentiality for commercial application.