Surface structure of few layer graphene

Understanding surface structure of graphene is important for its integration into composite materials. Here, we have used synchrotron X-ray reflectivity (XRR) to study the structure of commercially available graphene samples (prepared via chemical vapor deposition, and marketed as graphene monolayer...

Full description

Saved in:
Bibliographic Details
Published in:Carbon (New York) 2018-09, Vol.136, p.255-261
Main Authors: Zhou, Liangzhi, Fox, Laura, Włodek, Magdalena, Islas, Luisa, Slastanova, Anna, Robles, Eric, Bikondoa, Oier, Harniman, Robert, Fox, Neil, Cattelan, Mattia, Briscoe, Wuge H.
Format: Article
Language:English
Subjects:
Atomic force microscopy
Carbon
Chemical vapor deposition
Composite materials
Contaminants
Graphene
Morphology
Multilayers
Organic chemistry
Photoelectric emission
Silicon dioxide
Surface structure
Synchrotron radiation
Temperature dependence
Temperature effects
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Understanding surface structure of graphene is important for its integration into composite materials. Here, we have used synchrotron X-ray reflectivity (XRR) to study the structure of commercially available graphene samples (prepared via chemical vapor deposition, and marketed as graphene monolayers) on SiO2/Si at different temperatures. X-ray photoelectron spectroscopy, photoemission electron microscopy and atomic force microscopy (AFM) were employed to evaluate the composition and morphology of the graphene layer. Our results indicate that the samples we characterized consisted of 3–4 layers of graphene, which should thus be more accurately described as few layer graphene (FLG). Furthermore, a “contaminant” layer, comprising polymethylmethacrylate and graphene multilayers, was found present atop FLG. We also report tentative results on the effect of temperature on the graphene sample thickness. At 25 °C, the FLG thickness from XRR measurements was 13.0 ± 1.0 Å, in agreement with that obtained from AFM (13.9 ± 0.7 Å). Upon heating to 60 °C, the FLG thickness expanded to 13.8 Å, which further increased to 14.3 Å upon cooling to 25 °C. We attribute this temperature dependent thickness to the out-of-plane rippling of graphene as previously reported. These unprecedented results on the FLG surface structure are valuable to its potential bioanalytical applications. [Display omitted]
ISSN:0008-6223
1873-3891
DOI:10.1016/j.carbon.2018.04.089