Electrochemical Corrosion Behavior of Monel Alloy in Carbonate Melts

The interaction of the monel alloy and its corrosion resistance in a melt of alkali metal carbonates in an oxidizing atmosphere was studied. The selectivity of alloy dissolution and modification of the electrode surface after storage at a constant anode potential were analyzed. The generation and de...

Full description

Saved in:
Bibliographic Details
Published in:Russian journal of electrochemistry 2018-09, Vol.54 (9), p.697-701
Main Authors: Nikitina, E. V., Kazakovtseva, N. A., Maikov, M. A., Malkov, V. B., Karfidov, E. A., Chuikin, A. Yu
Format: Article
Language:English
Subjects:
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:The interaction of the monel alloy and its corrosion resistance in a melt of alkali metal carbonates in an oxidizing atmosphere was studied. The selectivity of alloy dissolution and modification of the electrode surface after storage at a constant anode potential were analyzed. The generation and development of local corrosion defects (pit corrosion, intercrystallite corrosion, corrosion cracking) on monel alloy (70% nickel, 28% copper), copper, and nickel electrodes in the molten eutectic of lithium, sodium, and potassium carbonates at a working temperature of 773 K were studied. The anode polarization was accompanied by a change in the state of the electrode surface.
ISSN:1023-1935
1608-3342
DOI:10.1134/S1023193518090082