Dipole pinning effect on photovoltaic characteristics of ferroelectric BiFeO3 films

Ferroelectric bismuth ferrite is an attractive candidate for switchable devices. The effect of dipole pinning due to the oxygen vacancy layer on the switching behavior of the BiFeO3 thin film fabricated by the chemical solution deposition method was studied after annealing under air, O2, and N2 envi...

Full description

Saved in:
Bibliographic Details
Published in:Journal of applied physics 2018-01, Vol.123 (2)
Main Authors: Biswas, P. P., Thirmal, Ch, Pal, S., Murugavel, P.
Format: Article
Language:English
Subjects:
Annealing
Applied physics
Bismuth ferrite
Deoxidizing
Dipoles
Electrical properties
Ferroelectric materials
Ferroelectricity
Leakage current
Open circuit voltage
Organic chemistry
Oxygen
Photoelectric effect
Photoelectric emission
Photovoltaic effect
Pinning
Switching
Thin films
Vacancies
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Ferroelectric bismuth ferrite is an attractive candidate for switchable devices. The effect of dipole pinning due to the oxygen vacancy layer on the switching behavior of the BiFeO3 thin film fabricated by the chemical solution deposition method was studied after annealing under air, O2, and N2 environment. The air annealed film showed well defined and dense grains leading to a lower leakage current and superior electrical properties compared to the other two films. The photovoltage and transient photocurrent measured under positive and negative poling elucidated the switching nature of the films. Though the air and O2 annealed films showed a switchable photovoltaic response, the response was severely affected by oxygen vacancies in the N2 annealed film. In addition, the open circuit voltage was found to be mostly dependent on the polarization of BiFeO3 rather than the Schottky barriers at the interface. This work provides an important insight into the effect of dipole pinning caused by oxygen vacancies on the switchable photovoltaic effect of BiFeO3 thin films along with the importance of stoichiometric, defect free, and phase pure samples to facilitate meaningful practical applications.
ISSN:0021-8979
1089-7550
DOI:10.1063/1.5006311