Mechanism of β-FeSi2 precipitates growth-and-dissolution and pyramidal defects' formation during oxidation of Fe-contaminated silicon wafers
Fe-implanted Si-wafers have been oxidized at 900 °C and 1100 °C in order to investigate the behaviour of Fe atoms at the growing SiO2/Si interface and the impact on the integrity of microelectronic devices of an involuntary Fe contamination before or during the oxidation process. As-implanted and ox...
Saved in:
Published in: | Journal of applied physics 2015-03, Vol.117 (11) |
---|---|
Main Authors: | , , , , , , |
Format: | Article |
Language: | English |
Subjects: | |
Citations: | Items that this one cites Items that cite this one |
Online Access: | Get full text |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Summary: | Fe-implanted Si-wafers have been oxidized at 900 °C and 1100 °C in order to investigate the behaviour of Fe atoms at the growing SiO2/Si interface and the impact on the integrity of microelectronic devices of an involuntary Fe contamination before or during the oxidation process. As-implanted and oxidized wafers have been characterized using secondary ion mass spectroscopy, atom probe tomography, and high-resolution transmission electron microscopy. Experimental results were compared to calculated implantation profiles and simulated images. Successive steps of iron disilicide precipitation and oxidation were evidenced during the silicon oxidation process. The formation of characteristic pyramidal-shaped defects, at the SiO2/Si interface, was notably found to correlate with the presence of β-FeSi2 precipitates. Taking into account the competitive oxidation of these precipitates and of the surrounding silicon matrix, dynamic mechanisms are proposed to model the observed microstructural evolution of the SiO2/Si interface, during the growth of the silicon oxide layer. |
---|---|