Unexpected ferromagnetic ordering enhancement with crystallite size growth observed in La0.5Ca0.5MnO3 nanoparticles

In this paper, the physical properties of half-doped manganite La0.5Ca0.5MnO3 with crystallite sizes ranging from 15 to 40 nm are investigated. As expected, ferromagnetic order strengthens at expense of antiferromagnetic one as crystallite size is reduced to 15 nm. However, contrary to previously re...

Full description

Saved in:
Bibliographic Details
Published in:Journal of applied physics 2014-09, Vol.116 (11)
Main Authors: Iniama, G., de la Presa, P., Alonso, J. M., Multigner, M., Ita, B. I., Cortés-Gil, R., Ruiz-González, M. L., Hernando, A., Gonzalez-Calbet, J. M.
Format: Article
Language:English
Subjects:
Antiferromagnetism
Coercivity
Core-shell structure
Crystallites
Ferromagnetism
Hysteresis loops
Magnetic saturation
Nanoparticles
Physical properties
Spin glasses
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:In this paper, the physical properties of half-doped manganite La0.5Ca0.5MnO3 with crystallite sizes ranging from 15 to 40 nm are investigated. As expected, ferromagnetic order strengthens at expense of antiferromagnetic one as crystallite size is reduced to 15 nm. However, contrary to previously reported works, an enhancement of saturation magnetization is observed as crystallite size increases from 15 to 22 nm. This unexpected behavior is accompanied by an unusual cell volume variation that seems to induce ferromagnetic-like behavior at expense of antiferromagnetic one. Besides, field cooled hysteresis loops show exchange bias field and coercivity enhancement for increasing cooling fields, which suggest a kind of core-shell structure with AFM-FM coupling for crystallite sizes as small as 15 nm. It is expected that inner core orders antiferromagnetically, whereas uncompensated surface spins behave as spin glass with ferromagnetic-like ordering.
ISSN:0021-8979
1089-7550
DOI:10.1063/1.4895707