Effects of glycerol monosterate on TPUs crystallization and its foaming behavior

• Main Authors: Hossieny, N, Nofar, M, Shaayegan, V, Park, C B
• Format: Conference Proceeding
• Language: English
• Subjects: Coalescing; Crystal structure; Crystallinity; Crystallization; Differential scanning calorimetry; Domains; Foaming; Foams; Glycerol; Lubrication; Morphology; Polyurethane resins; Synergistic effect; Urethane thermoplastic elastomers
• ISSN: 0094-243X; 1551-7616
• DOI: 10.1063/1.4873803

Thermoplastic polyurethane (TPU) containing 0-2 wt% glycerol monosterate (GMS) were compounded by a twin screw compounder and then foamed using a batch process and n-butane. Differential scanning calorimetry (DSC) and high-pressure DSC were performed to evaluate the effects of GMS and pressurized butane on the crystallization kinetics of TPU. The results showed that the synergistic effect of GMS and high pressure butane significantly promoted hard segment (HS) crystallization in the TPU-GMS samples. The TPU-GMS samples showed significant increase in crystallinity over a wide range of saturation temperatures in the presence of butane compared to neat melt-compounded TPU (PR-TPU). Comparing the foam characteristics of PR-TPU and TPU-GMS samples, it was observed that both samples exhibited microcellular morphology with high cell density over a wide range of processing temperatures of 150°C - 170°C. However at a high foaming temperature (170°C), PR-TPU foams showed high cell coalescence compared to TPU-GMS. Furthermore, TPU-GMS samples showed a much higher expansion ratio compared to PR-TPU over a wide range of processing temperatures. The lubricating effect of GMS assisted the HS to stack together and form crystalline domains. These HS crystalline domains are present at high temperature acting both as a heterogeneous nucleating sites as well as reinforcement leading to the observed microcellular morphology with a high expansion ratio in TPU-GMS samples.