Environmentally assisted cracking of forged 316LN stainless steel and its weld in high temperature water

•Fatigue CGRs of 316 LN and its weld were accelerated by high temperature water at lower frequencies (

Saved in:
Bibliographic Details
Published in:Corrosion science 2019-02, Vol.147, p.69-80
Main Authors: Du, Donghai, Wang, Jiamei, Chen, Kai, Zhang, Lefu, Andresen, Peter L.
Format: Article
Language:English
Subjects:
316LN stainless steel
Austenitic stainless steels
Base metal
Corrosion fatigue
Corrosion potential
Crack growth rate
Crack propagation
Delta ferrite
Dissolved oxygen
Environmentally assisted cracking
Fatigue cracking
Fatigue failure
Fracture mechanics
Frequency control
High temperature
Metallurgical analysis
Organic chemistry
Oxygenation
Pressurized water reactors
Stress corrosion cracking
Stress intensity factors
Water chemistry
Weld metal
Welded joints
δ-ferrite
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:•Fatigue CGRs of 316 LN and its weld were accelerated by high temperature water at lower frequencies (
ISSN:0010-938X
1879-0496
DOI:10.1016/j.corsci.2018.10.032