Fabrication and characterization of cellulose triacetate porous membranes by combined nonsolvent-thermally induced phase separation

Cellulose triacetate (CTA) porous membranes were firstly prepared by the combined nonsolvent-thermally induced phase separation (N-TIPS) method. Dimethyl sulfone (DMSO2) and polyethylene glycol (PEG400) were respectively chosen as the TIPS solvent and additive of CTA, while water was used as the NIP...

Full description

Saved in:
Bibliographic Details
Published in:Cellulose (London) 2019-04, Vol.26 (6), p.3747-3762
Main Authors: Xing, Xiao-Yan, Gu, Lin, Jin, Yu, Sun, Rui, Xie, Meng-Yun, Wu, Qing-Yun
Format: Article
Language:English
Subjects:
Bioorganic Chemistry
Cellulose
Cellulose triacetate
Ceramics
Chemistry
Chemistry and Materials Science
Coagulation
Composites
Glass
Mechanical properties
Membranes
Microfiltration
Morphology
Natural Materials
Organic Chemistry
Original Research
Phase separation
Physical Chemistry
Polyethylene glycol
Polymer Sciences
Pore size
Porosity
Solubility parameters
Substrates
Sustainable Development
Thin films
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Cellulose triacetate (CTA) porous membranes were firstly prepared by the combined nonsolvent-thermally induced phase separation (N-TIPS) method. Dimethyl sulfone (DMSO2) and polyethylene glycol (PEG400) were respectively chosen as the TIPS solvent and additive of CTA, while water was used as the NIPS nonsolvent. Their Hansen solubility parameters were analyzed to understand the solution thermodynamics. Detailed investigation was applied on the effects of the polymer concentration, the coagulation bath temperature and the coagulation bath composition on the CTA porous membranes. It is found that both NIPS and TIPS effects simultaneously exist and compete with each other, and further affect the membrane morphology and performance. The NIPS effect can be promoted by lowering the CTA concentration or elevating the coagulation bath temperature, resulting in figure-like macropores and porous top surface. The obtained CTA porous membranes show a water flux as high as 2002.9 ± 55.2 L/m 2 h. On the contrary, the TIPS effect becomes the dominant factor, and leads to the symmetric sponge-like pores, which facilitate to enhance the mechanical properties. Besides, CTA porous membranes present large surface pore size as well as low fraction of figure-like macropores as increasing the DMSO2 content in the coagulation bath. These CTA porous membranes with excellent water permeability and mechanical strength are promising candidates for microfiltration or the porous substrates of thin film composite membranes. Graphical abstract
ISSN:0969-0239
1572-882X
DOI:10.1007/s10570-019-02347-7