Monitoring critical defects of creep rupture in oriented strandboard using acoustic emission: incorporation of EN300 standard
This creep rupture study in commercial oriented strandboard (OSB) used a 4-point flexural test to evaluate the dynamic property changes of a 300x1,000-mm specimen using an acoustic emission (AE) system. Compared to deflection, AE events were more sensitive to damage accumulation than deflection to f...
Saved in:
Published in: | Wood science and technology 2005-05, Vol.39 (3), p.199-214 |
---|---|
Main Authors: | , , |
Format: | Article |
Language: | English |
Subjects: | |
Citations: | Items that this one cites Items that cite this one |
Online Access: | Get full text |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Summary: | This creep rupture study in commercial oriented strandboard (OSB) used a 4-point flexural test to evaluate the dynamic property changes of a 300x1,000-mm specimen using an acoustic emission (AE) system. Compared to deflection, AE events were more sensitive to damage accumulation than deflection to final failure. Specimens were artificially notched on either the tension- or compression-side and were subjected to 80% stress level at ambient conditions. Defects on the compression side of the bending specimen were found to be more critical than on the tension side in creep-rupture. The in-plane fractures followed patterns of the valleys of low-density spots as defect trenches, demonstrating adverse effects of high variation in horizontal density. An impetus and rationale to incorporate regulatory quality inspection standards and product certification of structural OSB based on the control limits of ±10% panel density as stipulated in EN300 standard is discussed. |
---|---|
ISSN: | 0043-7719 1432-5225 |
DOI: | 10.1007/s00226-004-0278-9 |