Improving the Properties of Aluminum Alloy System Al-Cu-Mg, Subjected to Hardening and Severe Plastic Deformation
The tendency of the aluminum alloy D16 system Al-Cu-Mg to natural (NA) and artificial aging (AA) after hardening and high pressure torsion (HPT) under a pressure of 6 GPa at room temperature was studied using optical metallography, scanning electron microscopy, electrical conductivity tests. The dep...
Saved in:
Published in: | Key engineering materials 2019-09, Vol.822, p.101-108 |
---|---|
Main Authors: | , , , |
Format: | Article |
Language: | English |
Subjects: | |
Citations: | Items that this one cites |
Online Access: | Get full text |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Summary: | The tendency of the aluminum alloy D16 system Al-Cu-Mg to natural (NA) and artificial aging (AA) after hardening and high pressure torsion (HPT) under a pressure of 6 GPa at room temperature was studied using optical metallography, scanning electron microscopy, electrical conductivity tests. The dependences of microhardness and electrical conductivity were constructed depending on the exposure time. It is shown that heat treatment (HT) (hardening + HPT + NA) leads to an increase of hardening of the alloy D16 compared to standard HT (T4) in 2,3 times, at preservation of level of conductivity. |
---|---|
ISSN: | 1013-9826 1662-9795 1662-9795 |
DOI: | 10.4028/www.scientific.net/KEM.822.101 |