In-situ TiC reinforced CoCrCuFeNiSi0.2 high-entropy alloy coatings designed for enhanced wear performance by laser cladding
In-situ synthesis of TiC reinforced CoCrCuFeNiSi0.2 high-entropy alloy (HEA) coatings were fabricated on the surface of 304 stainless steels by laser cladding. The influence of Ti and C addition on the phase composition and microstructure of the CoCrCuFeNiSi0.2 HEA composite coatings reinforced by (...
Saved in:
Published in: | Materials chemistry and physics 2020-02, Vol.242, p.122522, Article 122522 |
---|---|
Main Authors: | , , , , , |
Format: | Article |
Language: | English |
Subjects: | |
Citations: | Items that this one cites Items that cite this one |
Online Access: | Get full text |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Summary: | In-situ synthesis of TiC reinforced CoCrCuFeNiSi0.2 high-entropy alloy (HEA) coatings were fabricated on the surface of 304 stainless steels by laser cladding. The influence of Ti and C addition on the phase composition and microstructure of the CoCrCuFeNiSi0.2 HEA composite coatings reinforced by (Ti, C)x (x = 0, 0.5, 1.0, 1.5) were investigated by X-ray diffractometer, optical microscope and scanning electron microscope, respectively. The hardness and the room-temperature wear resistance of the HEA coatings were measured by Vickers hardness tester and dry sliding friction and wear tester. The experimental results show that the coatings without Ti and C consist of a single FCC solid solution structure. By the addition of Ti and C, the coatings consist of FCC solid solution and TiC. The microstructure of the HEA coatings are composed of typical dendrites. With the addition of Ti and C, the in-situ TiC ceramics are mainly distributed at the grain boundaries. Moreover, by further increase of the (Ti, C)x content, the volume fraction of the TiC ceramic in the composite coating is also gradually increased. The microhardness and wear resistance of the coatings with Ti and C additions are significantly improved, compared to those of the coatings without any such addition. Particularly, for the (Ti, C)1.0 coating, its average microhardness and wear volume is 498.5 HV0.2 and 0.42 mm3, respectively. In addition, the addition of Ti and C gradually reduce the coefficient of friction of the CoCrCuFeNiSi0.2 (Ti, C)x HEA coatings.
•In-situ TiC reinforced CoCrCuFeNiSi0.2 coatings are deposited by laser cladding.•The hardness and wear resistance of the coating are improved by Ti and C.•The CoCrCuFeNiSi0.2(Ti, C)1.0 HEA coating shows the best wear resistance. |
---|---|