Corrosion Behavior of AA 1100 Anodized in Gallic-Sulfuric Acid Solution

• Published in: Coatings (Basel) 2021, Vol.11 (4), p.405
• Main Authors: Mopon, Marlon L., Garcia, Jayson S., Manguerra, Dexter M., Narisma, Cyril John C.
• Format: Article
• Language: English
• Subjects: Aluminum base alloys; Anodizing; Caustic soda; Corrosion inhibitors; Corrosion resistance; Corrosion resistant alloys; Current density; Electrochemical impedance spectroscopy; Electrodes; Electrolytes; Gallic acid; Linear polarization; Organic acids; Protective coatings; Sulfuric acid
• ISSN: 2079-6412; 2079-6412
• DOI: 10.3390/coatings11040405

Sulfuric acid anodization is one of the common methods used to improve corrosion resistance of aluminum alloys. Organic acids can be added to the sulfuric acid electrolyte in order to improve the properties of the anodized aluminum produced. In this study, the use of gallic acid as an additive to the sulfuric acid anodization of AA1100 was explored. The effect of varying anodization current density and gallic acid concentration on the properties of anodized aluminum samples was observed using electrochemical impedance spectroscopy, linear polarization, and scanning electron microscopy. It was observed that the corrosion resistance of samples anodized in gallic-sulfuric acid solution at 10 mA·cm−2 is lower than samples anodized in sulfuric acid. It was also observed that higher anodization current density can lead to lower corrosion resistances for aluminum samples anodized in gallic-sulfuric acid solution. However, samples anodized at 5 mA·cm−2 and at a gallic acid concentration of 5 g·L−1 showed better corrosion performance than the samples anodized in sulfuric acid only. This suggests that the use of low amounts of gallic acid as an additive for sulfuric acid anodization can lead to better corrosion resistances for anodized aluminum.