Structural, chemical and magnetic features of gold nanoshapes integrated-Er2O3-doped tellurite glass system prepared by a conventional melt-quenching technique

• Published in: Applied physics. A, Materials science & processing Materials science & processing, 2021-09, Vol.127 (9), Article 673
• Main Authors: Salim, A. A., Mahraz, Z. A. S., Anigrahawati, P., Jan, N. A. M., Ghoshal, S. K., Sahar, M. R., Noor, F. M., Samah, K. A., Yaacob, S. N. S., Zain, S. K. MD, Aziz, M. S., Alias, S. S., Ahmad, N. H., Nurhafizah, H., Harun, A. N., Bakhtiar, H., Sazali, E. S.
• Format: Article
• Language: English
• Subjects: Applied physics; Characterization and Evaluation of Materials; Coercivity; Condensed Matter Physics; Erbium oxide; Functional groups; Glass; Gold; Heat treatment; Machines; Magnetic properties; Magnetic saturation; Manufacturing; Materials science; Metal ions; Morphology; Nanotechnology; Optical and Electronic Materials; Physics; Physics and Astronomy; Physiochemistry; Processes; Quenching; Structural analysis; Surfaces and Interfaces; Tellurium dioxide; Thin Films
• ISSN: 0947-8396; 1432-0630
• DOI: 10.1007/s00339-021-04841-x

Rare earth ions-doped oxide glasses with improved traits are needed for sundry applications. Based on this fact, physiochemical and magnetic characteristics of Er 3+ -doped lead–tellurite glasses embedded with gold nanoshapes (Au-NSPs) were customized via preparation and characterization. Glasses of composition 78.95TeO 2 –15PbO–5PbCl 2 –1Er 2 O 3 –0.05AuCl 3 were made using conventional melt-quenching techniques at varying (1, 6, 16, and 24 h) heat treatment durations (HTDs) to optimize their morphology, structure, chemical, and magnetic properties. Structure analysis verified the amorphous nature of the as-quenched samples and the homogeneous distribution of Au-NSPs within a network matrix with an average diameter ranged from 1.32 to 7.12 nm. Significant chemical functional groups of the glasses were detected at 360 and 598 cm ‒1 , attributed to the number of non-bridging oxygen (NBO) in glass and the conversion of TeO 4 tbp into TeO 3 polyhedra through TeO 3+1 . The magnetic behavior of the glasses was due to the diffusion-limited growth of Au-NSPs as evidenced from the ESR and VSM results. Saturation magnetization and magnetic coercivity were in the range of 4.61 × 10 –2 to 10.614 × 10 2  emu/g) and 1441.60 to 1992.20 Oe, respectively. The variations of g-factor , resonant magnetic field, and peak-to-peak line-width of the glasses were established to be promising for various functional applications especially for biomedical devices as antiviral screen protectors.